Abstract
This specification covers nickel-chromium-iron-molybdenum-copper alloy rods (UNS N06007, N06975, N06985, N06030, and N08031), hot- or cold-finished, solution annealed, ground, or turned, for use in general corrosive service. Heat and product (check) analysis of the alloy shall conform to the chemical composition requirements prescribed for nickel, chromium, iron, molybdenum, copper, manganese, cobalt, carbon, tungsten, silicon, phosphorus, sulfur, columbium and tantalum, titanium, and nitrogen. The material shall conform to the specified straightness criteria and to the mechanical property requirements including tensile strength, yield strength, and elongation, as determined by tension test.
Scope
1.1 This specification2 covers rod of Ni-Cr-Fe-Mo-Cu alloys (UNS N06007, N06975, N06985, N06030, N08031, and N08034)3 as shown in Tables 1-3, for use in general corrosive service.
TABLE 1 Chemical Requirements
Element
Composition Limits, %
Alloy
N06007
Alloy
N06975
Alloy
N06985
Alloy
N06030
Alloy
N08031
Alloy
N08034
Nickel
remainderA
47.0–52.0
remainderA
remainderA
30.0-32.0
33.5-35.0
Chromium
21.0–23.5
23.0–26.0
21.0–23.5
28.0–31.5
26.0-28.0
26.0-27.0
Iron
18.0–21.0
remainderA
18.0–21.0
13.0–17.0
remainderA
remainderA
Molybdenum
5.5–7.5
5.0–7.0
6.0–8.0
4.0–6.0
6.0-7.0
6.0-7.0
Copper
1.5–2.5
0.70–1.20
1.5–2.5
1.0–2.4
1.0-1.4
0.5-1.5
Manganese
1.0–2.0
1.0 max
1.0 max
1.5 max
2.0 max
1.0-4.0
Cobalt, max
2.5
…
5.0 max
5.0 max
…
…
Carbon, max
0.05
0.03
0.015 max
0.03 max
0.015
0.01
Tungsten
1.0 max
…
1.5 max
1.5–4.0
…
…
Silicon, max
1.0
1.0
1.0 max
0.8 max
0.3
0.1
Phosphorus, max
0.04
0.03
0.04 max
0.04 max
0.020
0.020
Sulfur, max
0.03
0.03
0.03 max
0.02 max
0.010
0.010
Columbium + tantalum
1.75–2.50
…
0.50 max
0.30–1.50
…
…
Titanium
…
0.7–1.5
…
…
…
…
Nitrogen
0.15-0.25
…
…
…
…
0.10-0.25
Aluminum
0.3
(A) See 13.1.1.
TABLE 2 Mechanical Property Requirements
Alloy
Specified Diameter, in. (mm)
Tensile Strength min, psi (MPa)
Yield Strength (0.2 % Offset), min, psi (MPa)
Elongation in 2 in. or 50.8 mm or 4D A min
N06007
5/16 to 3/4 (7.94 to 19.05), incl
90 000 (621)
35 000 (241)
35
Over 3/4 to 31/2 (19.05 to 88.9), incl
85 000 (586)
30 000 (207)
30
N06975
5/16 to 31/2 (7.94 to 88.9), incl
85 000 (586)
32 000 (221)
40
N06985
5/16 to 3/4 (7.9 to 19.05), incl
90 000 (621)
35 000 (241)
45
Over 3/4 to 31/2 (19.05 to 88.9), incl
85 000 (586)
30 000 (207)
35
N06030
…
85 000 (586)
35 000 (241)
30
N08031
All sizes
94 000 (648)
40 000 (276)
40
N08034
All sizes
94 000 (650)
40 000 (280)
40
(A) D refers to the diameter of the tension specimen.
TABLE 3 Permissible Variations in Diameter and Out-of-Roundness of Rods
Specified Diameter, in. (mm)
Permissible Variations, in. (mm)
Diameter
Out-of-Roundness, max
+
−
Hot-Finished, Annealed, and Descaled Rods
5/16 to 7/16 (7.94 to 11.11), incl
0.012 (0.305)
0.012 (0.305)
0.018 (0.457)
Over 7/16 to 5/8 (11.11 to 15.87), incl
0.014 (0.355)
0.014 (0.355)
0.020 (0.508)
Over 5/8 to 3/4 (15.87 to 19.05), excl
0.016 (0.406)
0.016 (0.406)
0.024 (0.610)
Hot-Finished, Annealed, and Ground or Turned Rods
3/4 to 31/2 (19.05 to 88.9), incl
0.010 (0.254)
0
0.008 (0.203)
1.2 The following products are covered under this specification:
1.2.1 Rods 5/16 to 3/4 in. (7.94 to 19.05 mm) excl in diameter, hot- or cold-finished, solution annealed and pickled or mechanically descaled.
1.2.2 Rods 3/4 to 31/2 in. (19.05 to 88.9 mm) incl in diameter, hot- or cold-finished, solution annealed, ground or turned.
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health and environmental practices, and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.