Significance and Use 4.1 The term “reference” as employed in this practice implies that either the glass or the metal of the reference glass-metal seal will be a “standard reference material” such as those supplied for other physical tests by the National Institute of Standards and Technology, or a secondary reference material whose sealing characteristics have been determined by seals to a standard reference material (see NBS Special Publication 260). Until standard reference materials for seals are established by the NIST, secondary reference materials may be agreed upon between manufacturer and purchaser.Scope 1.1 This practice covers the preparation and testing of a reference glass-metal sandwich seal for determining stress in the glass or for determining the degree of thermal expansion (or contraction) mismatch between the glass and metal. Tests are in accordance with Test Method F218 (Section 2). 1.2 This practice applies to all glass and metal (or alloy) combinations normally sealed together in the production of electronic components. 1.3 The practical limit of the test in deriving mismatch is approximately 300 ppm, above which the glass is likely to fracture. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.